Hunting Knife (How Products are Made)
The hunting knife is an ancient tool that has survived essentially unchanged to the present day. Belonging to the generation of tools or weapons after stones and clubs, the hunting knife gave early hunters the ability to butcher animals for meat and skins. It was also important to their defense from predators and warring tribes.
The first metal hunting knives were made of bronze around 2000 B.C., a time generally referred to as the Bronze Age. During 1500 to 1100 B.C., knives served as patterns for larger swords in Crete and Britain. With the coming of the Iron Age in the period 1000 to 800 B.C., the use of iron for the manufacture of knives developed. Iron allowed a sharper, more durable cutting edge than bronze. The major problem with iron knives was that they bent easily. The Vikings solved this problem by adding carbon, or "carbonizing" the iron. This hardened the iron blade and improved its rigidity and sharpness.
In early American history, one particular design of the hunting knife became a standard by which others were compared. This favorite of the early frontiersmen was the Bowie knife, named after the legendary pioneer James Bowie (1796-1836). This single-edged knife was 10-15 inches (25-38 cm) long. The steel blade was straight for most of its length with a concave tapered point.
The modern hunting knife usually has a rigid, single-edged blade with a handle large enough to be grasped firmly. The unsharpened portion of the blade, or tang, extends through the grip area for strength. Folding, lock-back knives and specialized skinning and gutting knives are also used for hunting and dressing game, but the basic, straight hunting knife is the outdoor enthusiast's standard.
The most important part of the modern hunting knife, the blade, is made of steel or stainless steel. Of particular importance is the carbon content of the metal, which determines the hardness of the blade. Other substances, such as molybdenum, produce other specific improvements in sharpness, toughness, finish, and corrosion resistance.
The guard and pommel may be steel, brass, or aluminum. The stocks, or grips, can be made of many materials. Some knifemakers use exotic woods or animal bone and horn for the stock. Stocks may also be wrapped with leather, or the leather may be in washer-like segments stacked on the tang and contoured to form the entire handle. The materials chosen for the stocks depend greatly on the desired use. More durable, utilitarian materials such as nylon and leather are chosen for knives intended for actual field use, while fancy materials are used for show knives.
The Manufacturing Process
Forming the blade
- 1 The blade begins as a "blank," cut from flat material that is in a "soft" condition, which means it has not been heat treated. Mass-produced knives are stamped in a
Image Pop-UpThe most important part of the modern hunting knife, the blade, is made of steel or stainless steel. Of particular importance is the carbon content of the metal, which determines the hardness of the blade.
After the blank is cut, holes for the handle stocks are drilled into the tang. Rough shaping is also performed by grinding or machining. This shaping forms the thickness of the blade at various points and reduces the amount of finish grinding on the sharp edge. Any identifying markings or decorative details are stamped while the blade is in a soft condition.
- 2 The blade is hardened to preserve the sharpness of the knife edge. Each blade material may require different hardening and heat-treating methods; however, common steel blades are generally heat treated in the following manner.
To harden the blade, several blades are placed into a ceramic tray in a heat-treating oven. They are laid flat so the weight of the blades does not cause warping. Depending upon the specific requirements of the alloy, the temperature in the oven is raised to approximately 1600°F (871°C). After heating the blades for approximately two hours, the entire tray is removed from the oven and the blades are submerged in oil or water. This rapidly cools the blades and is called quenching. The quenching locks the metal crystals into an intricate microscopic pattern. This process also results in the metal becoming very brittle. After quenching, the blades are reheated to approximately 500°F (260°C). At this point, the metal has a slight dark-reddish color, and the crystals change their alignment slightly. Then the blades are allowed to cool slowly in a process called tempering. This toughens the metal while retaining some of the brittleness needed for fine sharpening. Further heating and cooling cycles may be used to harden other specialized alloys.
Polishing and sharpening
- 3 After the heat-treated blades are cool, they are polished and sharpened. Polishing is performed by machine or by hand. A flat belt sander is used to produce a smooth, even, "brushed" finish to the sides of the blade. This also polishes out any marks from the punch press operation and removes the surface residue from the heat-treat operation. Next the blade is placed into a grinding fixture that passes it through a series of grinding wheels. Each rotating wheel removes the correct amount of metal
Image Pop-UpHunting Knife
- 4 To the casual observer, the knife edge appears as simply the result of two intersecting surfaces. Upon closer examination, the true form of the edge is seen to consist of two distinctly separate sets of angles. The first is left by the rough grinding as explained above, while the second is the fine angle that actually forms the cutting edge. This edge is produced by a fine grinding operation called honing. The angle of the hone may be between 17 and 30 degrees to the axis of the blade, depending upon the blade application. A smaller angle will produce a sharper edge, but the edge will wear and become dull more quickly. A fine grinding hone, or "stone," is oiled and gently rubbed on the knife edge. This action produces the finest sharpened edge and is the only true method of properly sharpening a knife blade. When viewed under a microscope, the rough ground edge appears as a series of jagged points.
While sharp enough to cut adequately in this condition, the points wear easily and soon the sharpness
Assembly of the stocks, guard, and pommel
- 5 The stocks are riveted or pressed onto the tang of the knife blade. A buffing wheel is used to smooth the stocks and blend the rivet heads. In the case of a leather handle, the washer segments are stacked onto the tang starting at the guard. After the handle length is filled with leather, the pommel is pressed onto the end of the tang and secured with a pin or rivet. This squeezes the leather together, making a tight, easily gripped handle. The leather may be shaped using a grinding wheel and then sealed with a penetrating sealer. The guard and pommel can then be finished by polishing with the buffing wheel. Great care must be taken during the assembly and finishing process as not to damage the knife blade or ruin the sharp edge.
To insure a sharp edge and long life after sharpening, the heat treatment of the blade must be monitored. This is performed by measuring the Rockwell Hardness, a procedure in which the blade or a sample specimen is placed under a hardened point. A heavy weight is exerted upon the point, and the amount of penetration is measured. The dent left by this test is barely visible to the naked eye, and can be done under the handle where it will be hidden. Using various conversion scales, the hardness can then be compared with the desired standard.
Sharpness and finish of the blade are also important. Skilled technicians visually inspect the blade, including using a microscope to closely view the sharpened edge. Any defective blades are returned to the final finishing and honing operation for rework.
The finish of the handle and other portions of the knife are also visually inspected. In particular, show knives are meticulously examined for the slightest defect. Since these knives are a form of art, they will be closely scrutinized by the buyer; any visual defects would lessen the knife's value. Also, if the knife is a duplicate of an historical piece, specific design details and markings are important to the collector.
The design and construction of the hunting knife has changed little in the last 200 years, and little change is expected in the future. Advances in metallurgy will continue to offer knife manufacturers new steel alloys, which they will use to improve the hardness, durability, and finish of their product. Likewise, new plastics with improved impact resistance, formability, and surface finish will find applications as knife stocks, or grips.
These will be minor changes, though, and will not change the overall design. Today's hunting knife will continue to be a useful and valued tool for the outdoor enthusiast, and will be kept proudly to be handed down to future generations.
Where To Learn More
Boye, David. Step-by-Step Knifemaking: You Can Do It! Rodale Press, 1977.
Latham, Sid. Knifecraft: A Comprehensive Step-by-Step Guide to the Art of Knifemaking. Stackpole Books, 1978.
Peterson, Harold L. American Knives: The First History and Collectors' Guide. Scribner, 1980.
Cooper, D. "Points of Interest," Popular Mechanics, October 1993, pp. 65-69.
i>Douglas E. Betts